is a bimodal terpolymer LLDPE produced using the proprietary Borstar technology combining easy processability with outstanding sealing performance, good optics and superior mechanical properties.
1,5 g/10min (190 °C / 2,16kg)
is produced using the proprietary Borstar® bimodal terpolymer technology combining outstanding sealing performance with easy processabilty, good optics and superior mechanical properties.
is produced using the proprietary Borstar® bimodal terpolymer technology combining easy processing, stiffness/impact balance, excellent tensile properties and good optics.
1,3 g/10min (190 °C / 2,16kg)
0,3 g/10min (230 °C / 2,16kg)
is a high molecular weight, low melt flow rate polypropylene block copolymer with very high impact strength.
0,8 g/10min (230 °C / 2,16kg)
is a high density polyethylene intended for blow moulding of products with high stiffness and very good environmental stress crack resistance (ESCR).
0,23 g/10min (190 °C / 2,16kg)
is a natural, medium molecular weight, medium melt flow rate polypropylene block copolymer with an optimal mechanical properties balance resulting in high stiffness and very good impact strength both at room temperature and at low temperatures.
1,3 g/10min (230 °C / 2,16kg)
is a very high impact heterophasic copolymer based on proprietary Borstar Nucleation Technology (BNT).This grade exhibits excellent impact strength even at low temperatures with well-balanced stiffness properties.
7 g/10min (230 °C / 2,16kg)
is a heterophasic copolymer.This grade is intended for compression and injection moulding.The main features of this grade are good stiffness and impact resistance, very good processability, high melt strength and extremely low tendency to stress whitening.